Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
Manufacturer | LG Chemical |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | LG Chemical SH610S ABS, Excellent Surface, High Impact.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
Maximum Moisture Content | 0.010 | 0.010 | Extrusion Molding |
Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 94 | 94 | ASTM D785 |
Tensile Strength, Yield | 35.3 MPa @Thickness 3.20 mm |
5120 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
Elongation at Break | 35 % @Thickness 3.20 mm |
35 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
Elongation at Yield | >= 5.0 % @Thickness 3.20 mm |
>= 5.0 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
Flexural Yield Strength | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
Flexural Modulus | 1.96 GPa @Thickness 3.20 mm |
284 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
Izod Impact, Notched | 3.53 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
6.61 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
4.12 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
7.71 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
Vicat Softening Point | 94.0 °C @Load 5.00 kg |
201 °F @Load 11.0 lb |
50°C/h; ASTM D1525 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Zone 1 | 180 - 210 °C | 356 - 410 °F | Extrusion Molding |
Zone 2 | 190 - 230 °C | 374 - 446 °F | Extrusion Molding |
Zone 3 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
Zone 4 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
Adapter Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
Die Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
Melt Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
Roll Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Bottom, Extrusion |
70.0 - 90.0 °C | 158 - 194 °F | Middle, Extrusion | |
70.0 - 100 °C | 158 - 212 °F | Top, Extrusion | |
Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Extrusion Molding |
Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |