SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* SH1100A is a Nylon 12, High Specificy Gravity compound containing proprietary fillers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 11.0 g/cc | 11.0 g/cc | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 0.50 % | 0.50 % | Type I, 5 mm/min; ASTM D638 |
| 0.50 % | 0.50 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.73 GPa | 686 ksi | 1 mm/min; ISO 527 |
| 11.16 GPa | 1619 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 38.0 MPa | 5510 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 38.0 MPa | 5510 psi | ISO 178 | |
| Flexural Yield Strength | 42.0 MPa | 6090 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.70 GPa | 1260 ksi | 2 mm/min; ISO 178 |
| 10.9 GPa | 1580 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.650 J/cm | 1.22 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.880 J/cm | 1.65 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Microcell Composite Company CELLIFF® 7000 Polymer Pellets
- Techmer ES HiFill® PC GF40 40% Glass Filled
- SABIC Innovative Plastics LNP Thermocomp OF004AER PPS (Asia Pacific)
- Teknor Apex Chemlon® ALF20 Nylon 66, Unreinforced
- Borealis Borseal™ RE239CF Polypropylene Copolymer
- Polyplastics Duranex® 300FP Polybutylene Terephthalate (PBT), Unfilled PBT for film, Extrusion, High Flow
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A
- ExxonMobil LDPE LD 313.NF Low Density Polyethylene Resin
- CMW® ELKONIUM 40 pure palladium
- Abatron 8311-8A/82033B Filled Potting Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved