Teknor Apex Monprene® MP-1885-L3 Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Teknor Apex Company |
| Trade Name | MONPRENE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Monprene® MP-1885-L3 Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Forms: Pellets Processing Method: Extrusion; Injection Molding Injection Notes: Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C); Injection Rate: Fast Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Melt Flow | 2.00 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.00 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | ASTM D2240 |
| Tensile Strength at Break | 23.4 MPa | 3400 psi | ASTM D412 |
| Tensile Stress | 8.96 MPa @Strain 300 % |
1300 psi @Strain 300 % |
ASTM D412 |
| Elongation at Break | 500 % | 500 % | ASTM D412 |
| Compression Set | 15 % @Temperature 22.8 °C |
15 % @Temperature 73.0 °F |
ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 232 °C | 360 - 450 °F | |
| Middle Barrel Temperature | 188 - 238 °C | 370 - 460 °F | |
| Front Barrel Temperature | 193 - 243 °C | 380 - 470 °F | |
| Nozzle Temperature | 199 - 249 °C | 390 - 480 °F | |
| Zone 1 | 182 - 232 °C | 360 - 450 °F | |
| Zone 2 | 188 - 238 °C | 370 - 460 °F | |
| Zone 3 | 193 - 243 °C | 380 - 470 °F | |
| Zone 5 | 199 - 249 °C | 390 - 480 °F | |
| Die Temperature | 199 - 249 °C | 390 - 480 °F | |
| Melt Temperature | 199 - 249 °C | 390 - 480 °F | Processing Temperature |
| Mold Temperature | 35.0 - 48.9 °C | 95.0 - 120 °F | |
| Injection Pressure | 1.38 - 5.52 MPa | 200 - 800 psi | |
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | |
| Cushion | 0.381 - 2.54 cm | 0.150 - 1.00 in | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Translucent |
Users viewing this material also viewed the following:
- Polyplastic Armlen® PP MF 25-3-901 Polypropylene, 20% Mineral Filled
- SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS (Europe-Africa-Middle East)
- Resinlab® CYNERGY CA6701 Adhesive
- Mearthane Durethaneâ„¢ S DS-555D Solid Polyurethane Elastomer
- SPS Guang Zhou REMAKâ„¢ 7001RM4 Flame-retarded PS masterbatch
- Dyna-Purge® C Purging Compound
- Samyang Trirex® 3025G15 Polycarbonate, 15% Glass Reinforced
- DuPont Elvaloy® 1209 AC Ethylene and 9% Methyl Acrylate Copolymer
- ExxonMobil Oppalyte™ 40MH247 OPP Film
- Dow UNIVAL™ DMDA-6200 NT 7 High Density Polyethylene Resin (HDPE)
Copyright © lookpolymers.com All Rights Reserved