LG Chemical SG175NS ABS, Super Surface Gloss, General Anti-Static
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | LG Chemical SG175NS ABS, Super Surface Gloss, General Anti-Static.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, Super Surface Gloss, General Anti-StaticApplication: Electric & Electronic ProductsCAS No. 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0040 - 0.0070 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 32 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 °C |
32 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Yield | 48.1 MPa <br>@Thickness 3.20 mm |
6970 psi <br>@Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 25 % <br>@Thickness 3.20 mm |
25 % <br>@Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 78.5 MPa <br>@Thickness 3.20 mm |
11400 psi <br>@Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa <br>@Thickness 3.20 mm |
370 ksi <br>@Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.16 J/cm <br>@Thickness 6.40 mm,<br> Temperature 23.0 °C |
4.04 ft-lb/in <br>@Thickness 0.252 in,<br> Temperature 73.4 °F |
ASTM D256 |
| 2.16 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C |
4.04 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C <br>@Thickness 6.40 mm |
185 °F <br>@Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Nozzle Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V75N Fluoroelastomer Compound
- Quadrant EPP Duratron® PI D7015G PI Bearing Grade Polyimide (ASTM Product Data Sheet)
- Kinlead LSD13 Low Temperature Grade Heat Sealable Film (thickness: 18 µm)
- Momentive Performance Materials XE23-B2484 Heat Cured Rubber - Electro Conductive
- A. Schulman POLYBATCH™ White 8350/UV5 Concentrate Based In Polyethylene
- Polyram Metal Cap PL380Z81 Heavy Density Polyethylene, 81% Mineral Filled
- Multibase Multi-ABS 3246 High Flow Grade
- Ineos Nova 3590 General Purpose Crystal Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved