LG Chemical RS657L ABS, Chemical Resistance to Cyclopentane, Low Specific Gravity

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical RS657L ABS, Chemical Resistance to Cyclopentane, Low Specific Gravity.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Extrusion Molding, Chemical Resistance to Cyclopentane, Thin ThicknessApplication: Refrigerator Inner LinerCAS No. 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Extrusion Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 4.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 4.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 101
101
ASTM D785
Tensile Strength, Yield 46.1 MPa

@Thickness 3.20 mm
 6680 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 35 %

@Thickness 3.20 mm
 35 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 5.0 %

@Thickness 3.20 mm
 >= 5.0 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 74.5 MPa

@Thickness 3.20 mm
 10800 psi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.40 GPa

@Thickness 3.20 mm
 348 ksi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 3.92 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 7.35 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
4.61 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 8.63 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 1.57 J/cm

@Thickness 6.40 mm,
Temperature -20.0 °C
 2.94 ft-lb/in

@Thickness 0.252 in,
Temperature -4.00 °F
 ASTM D256
1.67 J/cm

@Thickness 3.20 mm,
Temperature -20.0 °C
 3.12 ft-lb/in

@Thickness 0.126 in,
Temperature -4.00 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C

@Thickness 6.40 mm
 201 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C

@Thickness 6.40 mm
 192 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 96.0 °C

@Load 5.00 kg
 205 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Processing Properties Metric English Comments
Zone 1 180 - 210 °C
356 - 410 °F
Extrusion Molding
Zone 2 190 - 230 °C
374 - 446 °F
Extrusion Molding
Zone 3 200 - 250 °C
392 - 482 °F
Extrusion Molding
Zone 4 200 - 250 °C
392 - 482 °F
Extrusion Molding
Adapter Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Die Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Melt Temperature 200 - 250 °C
392 - 482 °F
Extrusion Molding
Roll Temperature 60.0 - 90.0 °C
140 - 194 °F
Bottom, Extrusion
70.0 - 90.0 °C
158 - 194 °F
Middle, Extrusion
70.0 - 100 °C
158 - 212 °F
Top, Extrusion
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Extrusion Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Extrusion Molding