DuPont™ Surlyn® 8527 Ionomer Resin, Sodium (discontinued **)
| Category | Polymer , Thermoplastic , Ionomer , Ionomer, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont™ Surlyn® 8527 Ionomer Resin, Sodium
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Surlyn® 8527 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neutralization levels for this grade result in excellent clarity and abrasion resistance. The resin can be injection or blow molded, and is processable by extrusion into sheets or shapes. It complies with the provisions of U.S. Food and Drug Administration (FDA) Title 21 Code of Regulations 177:1330 - ionomer resins.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | 50 mm/min cross speed; ASTM D638 |
| Elongation at Break | 450 % | 450 % | ASTM D638 |
| Flexural Modulus | 0.220 GPa | 31.9 ksi | ASTM D790 |
| Izod Impact, Notched | 6.10 J/cm | 11.4 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 1160 kJ/m² | 552 ft-lb/in² | ASTM D1822S |
| Abrasion | 600 | 600 | NBS Index; ASTM D1630 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature -20.0 - 32.0 °C |
77.8 µin/in-°F @Temperature -4.00 - 89.6 °F |
ASTM D696 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | |
| Melting Point | 93.0 °C | 199 °F | DTA |
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
| Vicat Softening Point | 73.0 °C | 163 °F | Rate B, ASTM D1525-70 |
| Brittleness Temperature | -95.0 °C | -139 °F | ASTM D746 |
| Flame Spread | 22.9 mm/min | 0.902 in/min | ASTM D635 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.0 % @Thickness 6.35 mm |
6.0 % @Thickness 0.250 in |
ASTM D1003A |
| Gloss | 75 % | 75 % | 20° per ASTM D523-6 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 71 T 20 PP, 20% mineral filling
- Nilit FRIANYL B63 BR90 Nylon 6.6 for injection molding, 90% bronze filled
- Advanced Elastomer Systems Santoprene® 153-38 Thermoplastic Rubber (discontinued **)
- Gwent Electronic Materials C2011009D1 Curable Silver Range
- Lubriplate SYNXTREME FG-2 Calcium Sulfonate Complex Synthetic Food Machinery Grade Grease
- Wellman Wellamid® 22LHI3 XE-NBK1 Impact Modified Engineering Nylon 66
- Zhejiang Juner PC-A2-9 Top-Grade Flame Retardant UV-Resistant
- Tra-Con Tra-Bond 293-1 General Purpose Instrument Epoxy Adhesive
- DSM Stanyl® TE250F8 Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry)
- Fainplast Compounds AP 90/2 Flexible PVC, Flame Retardant Insulation
Copyright © lookpolymers.com All Rights Reserved