Bulk Molding Compounds BMC SLC 1000 Glass Reinforced Polyester

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC
Manufacturer BMC - Bulk Molding Compounds Inc.
Trade Name BMC
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bulk Molding Compounds BMC SLC 1000 Glass Reinforced Polyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BMC SLC 1000 is a medium strength, low-cost, glass reinforced polyester compound with adjustable shrinkage. It is V-0 flame arc and track resistant. UL® recognized. This material was formerly known as Glastic® SLC 1000.
Physical Properties Metric English Comments
Specific Gravity 1.95 - 2.01 g/cc
1.95 - 2.01 g/cc
Water Absorption 0.070 - 0.12 %
0.070 - 0.12 %
24 hours, 23°C
Linear Mold Shrinkage 0.029 cm/cm
0.029 in/in
Mechanical Properties Metric English Comments
Hardness, Barcol 40 - 50
40 - 50
Tensile Strength, Ultimate 27.6 - 34.5 MPa
4000 - 5000 psi
Flexural Strength 103 - 110 MPa
15000 - 16000 psi
Flexural Modulus 13.1 - 13.8 GPa
1900 - 2000 ksi
Compressive Strength 145 - 159 MPa
21000 - 23000 psi
Izod Impact, Notched 1.60 - 2.67 J/cm
3.00 - 5.00 ft-lb/in
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Dielectric Strength 11.1 kV/mm
282 kV/in
Short Time
Dissipation Factor 0.018

@Frequency 60 Hz
0.018

@Frequency 60 Hz
Condition A
0.022

@Frequency 60 Hz
0.022

@Frequency 60 Hz
Condition D
0.024

@Frequency 60 Hz
0.024

@Frequency 60 Hz
Condition A
0.030

@Frequency 60 Hz
0.030

@Frequency 60 Hz
Condition D
Arc Resistance 199.5 sec
199.5 sec
Track Resistance >= 66.67 sec
>= 66.67 sec
Processing Properties Metric English Comments
Mold Temperature 138 - 166 °C
280 - 330 °F