LG Chemical RS-650 ABS, Extrusion, General Purpose

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical RS-650 ABS, Extrusion, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by LG Chem
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ISO 2577
Melt Index of Compound 6.825 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 6.825 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 52.0 MPa
7540 psi
50 mm/min; ISO 527
Elongation at Break 30 %
30 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 76.0 MPa
11000 psi
2 mm/min; ISO 178
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 16.0 kJ/m²

@Temperature -30.0 °C
 7.61 ft-lb/in²

@Temperature -22.0 °F
 ISO 180
34.0 kJ/m²

@Temperature 23.0 °C
 16.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 80
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179
Charpy Impact, Notched 1.90 J/cm²

@Temperature -30.0 °C
 9.04 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
3.60 J/cm²

@Temperature 23.0 °C
 17.1 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 20.0 °C
 44.4 µin/in-°F

@Temperature 68.0 °F
 ISO 11359
CTE, linear, Transverse to Flow 87.0 µm/m-°C

@Temperature 20.0 °C
 48.3 µin/in-°F

@Temperature 68.0 °F
 ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
Annealed, 80°C, 4 hours; ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Annealed, 80°C, 4 hours; ISO 175
Vicat Softening Point 99.0 °C
210 °F
50 N, 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 93
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 93
Dielectric Constant 2.9

@Frequency 1e+6 Hz
 2.9

@Frequency 1e+6 Hz
 IEC 250
3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 IEC 250
Dielectric Strength 47.0 kV/mm
1190 kV/in
IEC 243
Dissipation Factor 0.0090

@Frequency 1e+6 Hz
 0.0090

@Frequency 1e+6 Hz
 IEC 250
Comparative Tracking Index 525 V
525 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 220 - 250 °C
428 - 482 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 2 - 4 hour
2 - 4 hour
Predrying