PolyOne Stat-Tech™ PC-08CF/000 FR V0 Polycarbonate (PC)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	PolyOne Corporation
Trade Name	Stat-Tech™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Stat-Tech™ PC-08CF/000 FR V0 Polycarbonate (PC).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.24 g/cc	1.24 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	86.2 MPa	12500 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	5.0 - 10 %	5.0 - 10 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	2.07 GPa	300 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	172 MPa	24900 psi	ASTM D790
Flexural Modulus	2.76 GPa	400 ksi	ASTM D790
Izod Impact, Notched	0.910 J/cm @Thickness 6.35 mm, Temperature 23.0 °C	1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	139 °C @Thickness 6.35 mm	282 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	133 °C @Thickness 6.35 mm	271 °F @Thickness 0.250 in	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 0.794 mm	V-0 @Thickness 0.0313 in	Internal Method
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	Internal Method
	V-0 @Thickness 3.15 mm	V-0 @Thickness 0.124 in	Internal Method

Electrical Properties	Metric	English	Comments
Surface Resistance	5.00e+8 - 5.00e+12 ohm	5.00e+8 - 5.00e+12 ohm	ASTM D257

Processing Properties	Metric	English
Rear Barrel Temperature	290 - 310 °C	554 - 590 °F
Middle Barrel Temperature	290 - 310 °C	554 - 590 °F
Front Barrel Temperature	290 - 310 °C	554 - 590 °F
Mold Temperature	80.0 - 110 °C	176 - 230 °F
Drying Temperature	120 - 130 °C	248 - 266 °F
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour

Descriptive Properties	Value	Comments
Additive	Antistatic
Features	Antistatic
	Electromagnetic Shielding (EMI)
	ESD Protection
	Flame Retardant
	Radio Frequency Shielding (RFI)
Filler / Reinforcement	Carbon Fiber Reinforcement, 8.0% Filler by Weight
Forms	Pellets
Generic Material	PC
Generic Name	Polycarbonate (PC)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Aerospace Applications
	Automotive Under the Hood
	Business Equipment
	Electrical/Electronic Applications
	Housings
	Printer Parts