Arlon 47091R012 0.012" (0.305 mm) Uncured Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 47091R012 0.012" (0.305 mm) Uncured Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Uncured RubberSide 2: Uncured RubberAppearance: Red silicone gum on polymer linerThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 38.1 - 114 microns
1.50 - 4.50 mil
Side 2
76.2 microns
3.00 mil
Polyethylene Interleave
102 microns
4.00 mil
Prime Coated 2113 Fiberglass, Substrate
88.9 - 165 microns
3.50 - 6.50 mil
Side 1
267 - 343 microns
10.5 - 13.5 mil
Overall
Mechanical Properties Metric English Comments
Hardness, Shore A 40 - 50
40 - 50
Compound Property
Tensile Strength 5.58 - 6.83 MPa
810 - 990 psi
Compound Property
Elongation at Break 450 - 550 %
450 - 550 %
Compound Property
Peel Strength >= 1.40 kN/m
>= 8.00 pli
[ppi], Bond Strength
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Flammability Test <= 6.0
<= 6.0
[in], Char Length; FAR 25.853 Appendix F, Part 1, Section A.1.i
<= 15
<= 15
[sec], Flame Time; FAR 25.853 Appendix F, Part 1, Section A.1.i
Electrical Properties Metric English Comments
Dielectric Strength >= 118 kV/mm
>= 3000 kV/in
Processing Properties Metric English Comments
Cure Time 15.0 min

@Temperature 177 °C
0.250 hour

@Temperature 350 °F
Recommended Cure Cycle
120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Red
Total Product Weight (oz/yd2) 11.6 - 13.6
Uncoated Fabric Break Strength 195 lb/in
Warp Direction, Substrate Property
75 lb/in
Fill Direction, Substrate Property