LG Chemical MP220 ABS, High Adhesion, Heat Resistance

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical MP220 ABS, High Adhesion, Heat Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Feature: Injection Molding, High Adhesion, Metal PlatingApplication: Automobiles Radiator Grill, MoldingCAS No. 9003-56-9 and 9003-54-7Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
<br>@Thickness 3.20 mm
 0.0040 - 0.0070 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 18 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 18 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength, Yield 44.1 MPa
<br>@Thickness 3.20 mm
 6400 psi
<br>@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 40 %
<br>@Thickness 3.20 mm
 40 %
<br>@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 74.5 MPa
<br>@Thickness 3.20 mm
 10800 psi
<br>@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.45 GPa
<br>@Thickness 3.20 mm
 356 ksi
<br>@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 2.55 J/cm
<br>@Thickness 6.40 mm,<br> Temperature 23.0 °C
 4.78 ft-lb/in
<br>@Thickness 0.252 in,<br> Temperature 73.4 °F
 ASTM D256
2.55 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 4.78 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 1.27 J/cm
<br>@Thickness 6.40 mm,<br> Temperature -30.0 °C
 2.39 ft-lb/in
<br>@Thickness 0.252 in,<br> Temperature -22.0 °F
 ASTM D256
1.27 J/cm
<br>@Thickness 3.20 mm,<br> Temperature -30.0 °C
 2.39 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
<br>@Thickness 6.40 mm
 203 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
<br>@Thickness 6.40 mm
 192 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 97.0 °C
<br>@Load 5.00 kg
 207 °F
<br>@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
 UL 746B
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical with Impact 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
 UL 746B
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical without Impact 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
 UL 746B
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
 UL 746B
Flammability, UL94 HB
<br>@Thickness >=1.50 mm
 HB
<br>@Thickness >=0.0591 in
HB
<br>@Thickness >=3.00 mm
 HB
<br>@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Dielectric Strength 29.0 kV/mm
737 kV/in
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
7.0 - 15 sec
<br>@Thickness >=1.50 mm
 7.0 - 15 sec
<br>@Thickness >=0.0591 in
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
30 - 60 arcs
<br>@Thickness 1.50 mm
 30 - 60 arcs
<br>@Thickness 0.0591 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Middle Barrel Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Front Barrel Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Nozzle Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Melt Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 68.6 - 88.3 MPa
9950 - 12800 psi
Injection Molding
Screw Speed <= 80 rpm
<= 80 rpm
Injection Molding