LG Chemical Lupoy 1300-12 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupoy 1300-12 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: LUPOY PC 1300-12 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Characteristics: Medium viscosity, No UV absorbers and No mold release agentApplications: Compounds, Appliances, Packaging applications and Non food contact applicationsCAS: 103598-77-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.32 % @Temperature 23.0 °C |
0.32 % @Temperature 73.4 °F |
equilibrium, 50% RH; ASTM D570 |
| 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.00070 cm/cm | 0.00050 - 0.00070 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 73 | 73 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 71.0 MPa | 10300 psi | ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | ASTM D638 |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 9.074 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
17.00 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
0.25 mm notch; ASTM D256 |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256 |
| Dart Drop, Total Energy | 87.0 J @Thickness 3.20 mm |
64.2 ft-lb @Thickness 0.126 in |
203m/min; ASTM D3763 |
| Abrasion | 45 @Load 1.00 kg |
45 @Load 2.20 lb |
[%], CS-10 F wheel, 500 cycles; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 68.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Hot Ball Pressure Test | >= 125 °C | >= 257 °F | IEC 598-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C @Thickness 4.00 mm |
291 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C @Thickness 4.00 mm |
264 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
| 141 °C @Thickness 4.00 mm |
286 °F @Thickness 0.157 in |
Annealed; ASTM D648 | |
| Vicat Softening Point | 149 °C @Load 5.10 kg |
300 °F @Load 11.2 lb |
50°C/hr; ASTM D1525 |
| Softening Point | 150 - 200 °C | 302 - 392 °F | melting point per MSDS |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
ASTM D635 |
| V-2 @Thickness 0.500 mm |
V-2 @Thickness 0.0197 in |
ASTM D635 | |
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
ASTM D635 | |
| V-2 @Thickness 2.50 - 2.70 mm |
V-2 @Thickness 0.0984 - 0.106 in |
ASTM D635 | |
| Flash Point | >= 450 °C | >= 842 °F | |
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
| Glow Wire Test | 850 °C @Thickness 2.00 mm, Time 5.00 sec |
1560 °F @Thickness 0.0787 in, Time 0.00139 hour |
IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542 |
| Haze | 0.70 - 1.5 % | 0.70 - 1.5 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60.0 Hz |
0.0010 @Frequency 60.0 Hz |
ASTM D150 |
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Autoignition Temperature | >450°C | |
| Average Extent of Burning | ASTM D635 |
Users viewing this material also viewed the following:
- Mallard Creek Polymers ROVENE® 4019 SBR Latex
- Momentive Performance Materials Silglaze® II Construction Sealant
- LyondellBasell Higlass SB224-1 Polypropylene Copolymer, 10% Glass Fiber
- Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK)
- Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled
- DuPont Elvax® 265 Ethylene-Vinyl Acetate Copolymer Resin
- Covestro Makrolon® FR 7087 Polycarbonate
- Abatron AboCast 8103-28 High-Performance Dielectric Epoxy
- Tisan TISOPLEN® 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved