LG Chemical LUSEP SP2300 SPS+GF30%, General Purpose

Category Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber
Manufacturer LG Chemical
Trade Name LUSEP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUSEP SP2300 SPS+GF30%, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, sPS+GF30%, General PurposeApplication: Pump Units, Pick-up Lends Holder, etc.CAS No. 9003-53-6 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0030 - 0.0090 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0090 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 118 MPa

@Thickness 3.20 mm
 17100 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 2.0 %

@Thickness 3.20 mm
 2.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 177 MPa

@Thickness 3.20 mm
 25600 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 8.83 GPa

@Thickness 3.20 mm
 1280 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.883 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.65 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 °C

@Thickness 6.40 mm
 500 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) >= 220 °C

@Thickness 6.40 mm
 >= 428 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Dielectric Strength 35.0 kV/mm

@Thickness 1.00 mm
 889 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 120 - 180 sec
120 - 180 sec
ASTM D495
Comparative Tracking Index 500 - 600 V
500 - 600 V
Solution A; IEC 60112
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=3.00 mm
 15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI 30 - 60 arcs

@Thickness 3.00 mm
 30 - 60 arcs

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 270 - 290 °C
518 - 554 °F
Injection Molding
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Injection Molding
Front Barrel Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Nozzle Temperature 280 - 310 °C
536 - 590 °F
Injection Molding
Melt Temperature 280 - 310 °C
536 - 590 °F
Injection Molding
Mold Temperature 80.0 - 150 °C
176 - 302 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Screw Speed 40 - 80 rpm
40 - 80 rpm
Injection Molding