SABIC Innovative Plastics LNP THERMOCOMP OC006 PPS - Linear (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP OC006 PPS - Linear (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* OC006 is a compound based on PPS - Linear resin containing Carbon Fiber. Added features include : Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 213 MPa | 30900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 26.6 GPa | 3860 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 250 MPa | 36300 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 298 MPa | 43200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 22.5 GPa | 3260 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C @Temperature 23.0 - 60.0 °C |
3.33 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 46.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
25.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 280 °C | 536 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 267 °C | 513 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66 (Unverified Data**)
- Overview of materials for Epoxy Encapsulant, Unreinforced
- Styrolution Styrolux® 656 C SBC
- Teknor Apex MONPRENE® MP 2840E Thermoplastic Elastomer
- SABIC Innovative Plastics Xenoy® XD1607 PBT+PC (Europe-Africa-Middle East)
- Teknor Apex Sinpolene MBB7532 Low Density Polyethylene
- Toyobo ECOVYLOPET® EMC2311 PET Bottle Recycling Grade, 10% Glass Reinforced
- Asahi Kasei Leona® 90G33 33% Glass Filled Nylon 66
- Outokumpu LDX 2101® Duplex Stainless Steel
Copyright © lookpolymers.com All Rights Reserved