LG Chemical LUPOY HR5007AE PC/ABS, High Impact

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOY HR5007AE PC/ABS, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PC/ABS, High Flow, High ImpactApplication: E&E (Housing)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
<br>@Thickness 3.20 mm
 0.0050 - 0.0080 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 5.5 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 5.5 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength, Yield 53.9 MPa
<br>@Thickness 3.20 mm
 7820 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 100 %
<br>@Thickness 3.20 mm
 >= 100 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 86.3 MPa
<br>@Thickness 3.20 mm
 12500 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.26 GPa
<br>@Thickness 3.20 mm
 327 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 4.41 J/cm
<br>@Thickness 3.20 mm,<br> Temperature -30.0 °C
 >= 8.27 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature -22.0 °F
 ASTM D256
>= 6.18 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 >= 11.6 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 108 °C
<br>@Thickness 6.40 mm
 226 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C
<br>@Thickness >=1.60 mm
 140 °F
<br>@Thickness >=0.0630 in
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C
<br>@Thickness >=1.60 mm
 140 °F
<br>@Thickness >=0.0630 in
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C
<br>@Thickness >=1.60 mm
 140 °F
<br>@Thickness >=0.0630 in
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
Flammability, UL94 HB
<br>@Thickness >=1.60 mm
 HB
<br>@Thickness >=0.0630 in
HB
<br>@Thickness >=3.00 mm
 HB
<br>@Thickness >=0.118 in
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
High Voltage Arc-Tracking Rate, HVTR >= 150 mm/min
>= 5.91 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Middle Barrel Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Front Barrel Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Nozzle Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Melt Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding