LG Chemical LUPOY HG5000B PC/ABS, Heat Resistance

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOY HG5000B PC/ABS, Heat Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PC/ABS, High Gloss, Heat Resistance, High FlowApplication: E&E (housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
<br>@Thickness 3.20 mm
 0.0050 - 0.0080 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 7.5 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 7.5 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ASTM D785
Tensile Strength, Yield 59.8 MPa
<br>@Thickness 3.20 mm
 8680 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 100 %
<br>@Thickness 3.20 mm
 >= 100 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 91.2 MPa
<br>@Thickness 3.20 mm
 13200 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.26 GPa
<br>@Thickness 3.20 mm
 327 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 5.49 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 >= 10.3 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 114 °C
<br>@Thickness 6.40 mm
 237 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
Flammability, UL94 HB
<br>@Thickness >=1.50 mm
 HB
<br>@Thickness >=0.0591 in
HB
<br>@Thickness >=3.00 mm
 HB
<br>@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Middle Barrel Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Front Barrel Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Nozzle Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection Molding
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding