LG Chemical LUPOY GP5008A PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP5008A PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, General Purpose, High FlowApplication: Miscellaneous GoodsCAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 39.2 MPa @Thickness 3.20 mm |
5690 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 59.8 MPa @Thickness 3.20 mm |
8680 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 1.67 GPa @Thickness 3.20 mm |
242 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.51 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 8.45 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Injection Molding |
| Front Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Injection Molding |
| Nozzle Temperature | 235 - 255 °C | 455 - 491 °F | Injection Molding |
| Melt Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Niche Polymer PPCG40BK Copolymer PP, 40% Glass Fiber Filled
- Pyrotek TS-550 Insulating Board
- Nilit Nilamid B3 H ZA Unfilled, Low Temperature Impact Resistant PA6
- ICO Polymers ICORENEâ„¢ 440-1312 PP Rotational Molding Resin
- Karina E 830-18/99-CRB Gray PVC Compound
- Multibase Multi-Flex® A 8502 LC UV RXF/YYWA Black TPE Thermoplastic Elastomer
- DuPont™ Nomex® Type 993, 80 mil Nominal Thickness Medium-Density Aromatic Nylon Pressboard
- ACC QM 100 QSI Quantum Silicones Clear 30 Durometer Condensation Cure Material
- 3M Dynamar™ RC 5115 Rubber Curative
Copyright © lookpolymers.com All Rights Reserved