LG Chemical LUPOY GP5006BH PC/ABS, Heat Resistance, Impact Strength
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP5006BH PC/ABS, Heat Resistance, Impact Strength.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, Heat Resistance, Impact Strength, High ToughnessApplication: Miscellaneous GoodsCAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.3 g/10 min @Load 2.16 kg, Temperature 250 °C |
3.3 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 56.9 MPa @Thickness 3.20 mm |
8250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 100 % @Thickness 3.20 mm |
>= 100 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 91.2 MPa @Thickness 3.20 mm |
13200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa @Thickness 3.20 mm |
327 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 5.39 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
>= 10.1 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256 |
| >= 7.06 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 13.2 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C @Thickness 6.40 mm |
241 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Front Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Nozzle Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection Molding |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 81 T 15 PP, 15% mineral filling
- Outokumpu 4845 High Temperature Austenitic Stainless Steel
- Palm Labs Adhesives TURBO FUSE SERIES 190-HT (4000 cp HIGH TEMPERATURE) Rapid Bonding Adhesive
- Lord Adhesives 513 Fast Cure, Non-Sagging Acrylic Adhesive
- Multibase Multi-Flex® TPE A 3104-10 AGATE 5ES
- Stir SpA AF 95 HT 105 CZ (PVC)
- Techmer ES Plaslube® J-1/AF/15/TF/10 NAT PA66
- 3M Scotch® 3779 Security Message Box Sealing Tape
- BASF Lupranate® 81 Isocyanate
Copyright © lookpolymers.com All Rights Reserved