LyondellBasell Hifaxâ„¢ AA56H Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ AA56H Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ AA56H medium high melt flow, 1,400 MPa flexural modulus, UL 94 V-2 flame retardant polypropylene homopolymer resin has an excellent combination of properties and processability. It was designed for applications that require flame and heat resistance, along with good electrical properties and surface quality. Uses: Appliances, electrical parts, household goodsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ASTM D 785 |
| Tensile Strength at Break | 29.0 MPa | 4200 psi | ASTM D 638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D 638 |
| Elongation at Break | 250 % | 250 % | ASTM D 638 |
| Flexural Modulus | 1.40 GPa | 203 ksi | 1% Secant, 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.689 J/cm | 1.29 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 2.00 J @Temperature -30.0 °C |
1.47 ft-lb @Temperature -22.0 °F |
ASTM D3029, tested in accordance with ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 115 °C | 239 °F | 0.118 in; UL 746 |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | 0.118 in; UL 746 |
| UL RTI, Mechanical without Impact | 115 °C | 239 °F | 0.118 in; UL 746 |
| Flammability, UL94 | V-2 | V-2 | 0.0591 in |
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
| Shrinkage | 1.7 % | 1.7 % | Tool, 100x150x3.2 mm Injection Molded Plaque; Basell Test Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.60e+16 ohm-cm | 7.60e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 42.9 kV/mm | 1090 kV/in | ASTM D149 |
| Arc Resistance | 88 sec | 88 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Polymer Resources NY66-IM1-[color]-H Nylon 66, Medium Impact Modified, Heat Stabilized
- SABIC Innovative Plastics Lexan® ML3982 PC (Europe-Africa-Middle East)
- LyondellBasell Montell 12C01G2 Clarity LLDPE
- Garlock GYLON® 3500 PTFE Gasketing, Silica Filler
- Techmer ES HiFill® PA6/6 GF30 HR L 30% Glass Filled
- Silberline Aquavet® 190nl-136M
- Samsung Cheil Industries TRANEX® TX-0520T Transparent Grade ABS
- Techmer ES Electrablend® PA6/6 03003 CF Carbon Filled
- TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), Typical
- BLUESTAR LXS 110 PPE-PS
Copyright © lookpolymers.com All Rights Reserved