SABIC Innovative Plastics Cycoloy® C2100 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C2100 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CYCOLOY C2100 is a flame retardant blend, specifically developed to meet the stringent requirements of mains current carrying applications. CYCOLOY C2100 combines
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 15 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 58.0 MPa
8410 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 70 %
70 %
Type I, 5 mm/min; ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.20 J/cm
11.6 ft-lb/in
ASTM D256
Charpy Impact, Notched 5.00 J/cm²
23.8 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 1.8 MPa (264 psi) 118 °C

@Thickness 6.40 mm
 244 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 125 °C
257 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 115 °C
239 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
5VB

@Thickness 2.00 mm
 5VB

@Thickness 0.0787 in
 UL 94
Oxygen Index 32 %
32 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.6

@Frequency 1.00e+6 Hz
 2.6

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 50.0 - 60.0 Hz
 3.0

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
 432 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
 635 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
 889 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.0050

@Frequency 50.0 - 60.0 Hz
 0.0050

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0080

@Frequency 1.00e+6 Hz
 0.0080

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 225 V
225 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2