LG Chemical LUPOY GP2102 PC+GF10%
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP2102 PC+GF10%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC+GF10%, General Purpose, Good Toughness, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 124 | 124 | ASTM D785 |
| Tensile Strength, Yield | 54.9 MPa @Thickness 3.20 mm |
7970 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 20 % @Thickness 3.20 mm |
20 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 108 MPa @Thickness 3.20 mm |
15600 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 3.24 GPa @Thickness 3.20 mm |
469 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 2.94 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 5.51 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C @Thickness 0.750 - 0.800 mm |
176 °F @Thickness 0.0295 - 0.0315 in |
|
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 0.750 - 0.800 mm |
176 °F @Thickness 0.0295 - 0.0315 in |
|
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness 0.750 - 0.800 mm |
176 °F @Thickness 0.0295 - 0.0315 in |
|
| Flammability, UL94 | HB @Thickness 0.750 - 0.800 mm |
HB @Thickness 0.0295 - 0.0315 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 300 °C | 518 - 572 °F | Injection Molding |
| Middle Barrel Temperature | 280 - 310 °C | 536 - 590 °F | Injection Molding |
| Front Barrel Temperature | 290 - 330 °C | 554 - 626 °F | Injection Molding |
| Nozzle Temperature | 290 - 330 °C | 554 - 626 °F | Injection Molding |
| Melt Temperature | 300 - 340 °C | 572 - 644 °F | Injection Molding |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | Injection Molding |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Parker Chomerics ECOPLATE™ 5030
- Ensinger ENSILON® 6/6 GF30 Extruded Nylon 6/6, 30% glass-fiber-reinforced (PA66) (discontinued **)
- Sylvin Technologies 9980-95 Natural PVC Molding Compound
- SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Europe-Africa-Middle East)
- Skamol Group V-LITE 475 Vermiculite Insulating Brick
- Hexcel® HexWeb® HRH-10 - 3/16 - 1.5 Aramid Fiber/Phenolic Resin Honeycomb
- DSM EcoPaXX® Q-E7300 PA410-I
- ChevronTexaco Meropa® 320
- 3M Scotchkote™ HB 850 Epoxy Floor Coating
- DuPont Performance Polymers Rynite® 530 BK503 PET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved