- Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- LG Chemical LUPOS GP-2201F General Purpose ABS, 20% Glass Fiber Reinforced, Flame Retardant
LG Chemical LUPOS GP-2201F General Purpose ABS, 20% Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUPOS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOS GP-2201F General Purpose ABS, 20% Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have a wide range of applications in automotive parts, electrical/electronic parts. and industrial equipments, etc.Applications: Automotive: Main core, glove box, meter box, head lamp housing, back mirror cover, etc.Electrical and Electronic: Computer tape reel, pan cake hub for video and audio, stereo speaker box, fan for air conditioner, washing machine pulley, fax frameOthers:Camera body, fishing reel, bobbinInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Temperature 23.0 °C |
0.918 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | |
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 90.0 °C | 194 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 78.45 - 88.26 MPa | 11380 - 12800 psi | Second |
| 68.65 - 98.07 MPa | 9957 - 14220 psi | First | |
| Back Pressure | 0.000 - 3.92 MPa | 0.000 - 569 psi | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V75L Fluoroelastomer Compound
- Kolon KOPA® KN333MS Low Friction Nylon 66
- LG Chemical PB1752 PVC
- Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 3.50 inch (88.9 mm) o.d. and 0.219 inch (5.49 mm) Thickness
- SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 (Asia Pacific)
- Westlake Epolene® C-17 Coating Grade - Highly Branched Medium Molecular Weight Polyethylene Polymer
- TIMET TIMETAL® 3-2.5 Titanium Alloy (Ti-3Al-2.5V; ASTM Grade 9) CWSR
- 3M 1120 EMI Shielding Tape
- Armstrong C-1/E Epoxy Adhesive
- Azdel Plus R301B01N 30% Continuous Random Fiber Mat / PP Resin Matrix
Copyright © lookpolymers.com All Rights Reserved