Lehmann & Voss LUVOCOM® 1105-8048 PEEK, with carbon fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-8048 PEEK, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0015 cm/cm | 0.00050 - 0.0015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 280 MPa | 40600 psi | |
| Elongation at Yield | 0.90 % | 0.90 % | |
| 1.1 % | 1.1 % | flexural | |
| Modulus of Elasticity | 49.0 GPa | 7110 ksi | |
| Flexural Strength | 400 MPa | 58000 psi | |
| Flexural Modulus | 41.0 GPa | 5950 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 300 °C | 572 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 330 °C | 626 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® NX9260 PTFE Laminate, Woven-Glass Reinforced
- Chevron Phillips 4538B LDPE Injection Molding Resin (discontinued **)
- LyondellBasell Plexar® PX1164 Extrudable Tie-Layer Resin - Anhydride Modified EVA
- Haysite SDL® H261 Polyester, Static Dissipative
- SABIC Innovative Plastics LNP STAT-KON DD000 PC (Asia Pacific)
- Shin-Etsu Silicones KE-1867 Silicone, RTV Adhesive/Sealant
- Wellman Wellamid® MRGST1715-WBK1 Nylon 6, 25% Mineral and Glass Sphere Reinforced, Impact Modified, Weatherable Grade
- ExxonMobil 320 Mobil DTE PM Series
- Aclo Accutech Polypropylene Homopolymer HP0336M10L Mica Reinforced
- Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 35% Cold Worked
Copyright © lookpolymers.com All Rights Reserved