ExxonMobil Enable™ 27-03HH Metallocene Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Exxon Chemical
Trade Name Enable™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Enable™ 27-03HH Metallocene Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Enable 23-05 resins are metallocene ethylene-hexane copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact and puncture. Easier processing and excellent properties lead to significant high pressure LDPE replacement in many applications, yet with superior drawdown and enhanced toughness. Enable 23-05 resins are available with and without antiblockAvailability: Latin America, North America and South AmericaAdditive:Antiblock: 2000 ppm Slip: No Processing Aid: Yes Thermal Stabilizer: YesApplications:Agricultural FilmBlown FilmCollation Shrink Food packagingForm Fill and Seal PackagingHeavy Duty BagsLamination FilmMultilayer Packaging FilmShrink FilmStand Up Pouches Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.927 g/cc
0.0335 lb/in³
ExxonMobil method
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 13.1 MPa
1900 psi
ASTM D882
Film Tensile Strength at Yield, TD 15.2 MPa
2200 psi
ASTM D882
Film Elongation at Break, MD 480 %
480 %
ASTM D882
Film Elongation at Break, TD 750 %
750 %
ASTM D882
Puncture Energy 2.94 J
2.17 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 40 g
40 g
ASTM D1922
Elmendorf Tear Strength TD 670 g
670 g
ASTM D1922
Dart Drop Test 140 g
0.309 lb
ASTM D1709A
Film Tensile Strength at Break, MD 64.1 MPa
9300 psi
ASTM D882
Film Tensile Strength at Break, TD 52.4 MPa
7600 psi
ASTM D882
1% Secant Modulus, MD 310 MPa
45000 psi
ASTM D882
1% Secant Modulus, TD 386 MPa
56000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 246 °C
<= 475 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 12 %
12 %
ASTM D1003
Gloss 42 %
42 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 11 lbf
ExxonMobil Method