- Clariant Renol PCSP0013WT-192 Polycarbonate, Flame Retardant, UV Stabilized, High Opacity
Clariant Renol PCSP0013WT-192 Polycarbonate, Flame Retardant, UV Stabilized, High Opacity
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant , Polycarbonate, UV Stabilized |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PCSP0013WT-192 Polycarbonate, Flame Retardant, UV Stabilized, High Opacity.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 49.6 MPa | 7200 psi | ASTM D638 |
| Flexural Yield Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 3.96 GPa | 575 ksi | ASTM D790 |
| Izod Impact, Notched | 3.84 J/cm @Temperature 22.8 °C |
7.20 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |
| Mold Temperature | 65.6 - 79.4 °C | 150 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 104 °C |
2 - 4 hour @Temperature 220 °F |
to ensure moisture content is less than 0.05% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Technetics Group Amicon™ PEEK 30% Carbon (Unverified Data**)
- Karina 48/1-FC-LMP (SDB) Black Color Concentrate for PVC
- Materion Beryllium Copper Alloy 25 Strip; 1/4HT (TH01) Temper (UNS C17200)
- SGL Carbon Group SIGRAFIL C® C25 P350 GLY Pelletized Carbon Fiber, Glycerine Sizing
- Saint-Gobain CHR® 6005 Glass-Foil Backing Silicone Adhesive Pressure Sensitive Tape
- ExxonMobil Pax-Plus™ 3208 Blown Film Resin
- ATI Allegheny Ludlum AL 304DA Stainless/Carbon Steel Three-Ply Composite
- Asahi Kasei Thermylene® P-20TC-5100 Chemically Coupled Polypropylene Compound, 20% Talc Filled
- Polyram RamSter PF353M6 PBT, 30% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved