Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets

Category	Polymer , Thermoplastic , Polyester, TP
Manufacturer	Elektro-Isola
Trade Name	G-Etronax
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free. Very mechanically very strong. Off white coloring. Applications: Used as an insulation material in electrotechnical applications such as plate-enclosed distribution systems, partition plates, and busbar carriers. .Information provided by Elektro-Isola

Physical Properties	Metric	English	Comments
Density	1.85 g/cc	0.0668 lb/in³	24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption	0.40 %	0.40 %	24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2

Mechanical Properties	Metric	English	Comments
Tensile Strength	100 MPa @Thickness >=1.50 mm	14500 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity	10.0 GPa @Thickness >=1.50 mm	1450 ksi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength	65.0 MPa @Thickness >=1.50 mm	9430 psi @Thickness >=0.0591 in	1hr/130°C/measured at 130°C; ISO 178; IEC/EN 60893-2 5.1
	200 MPa @Thickness >=1.50 mm	29000 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
	50.0 MPa @Treatment Temp. 200 °C, Time 3600 sec	7250 psi @Treatment Temp. 392 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	90.0 MPa @Treatment Temp. 150 °C, Time 3600 sec	13100 psi @Treatment Temp. 302 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	170 MPa @Treatment Temp. 100 °C, Time 3600 sec	24700 psi @Treatment Temp. 212 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	190 MPa @Treatment Temp. 50.0 °C, Time 3600 sec	27600 psi @Treatment Temp. 122 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
	200 MPa @Treatment Temp. 20.0 °C, Time 3600 sec	29000 psi @Treatment Temp. 68.0 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
Compressive Strength	300 MPa @Thickness >=5.00 mm	43500 psi @Thickness >=0.197 in	24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
	110 MPa @Treatment Temp. 200 °C, Time 3600 sec	16000 psi @Treatment Temp. 392 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	180 MPa @Treatment Temp. 150 °C, Time 3600 sec	26100 psi @Treatment Temp. 302 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	250 MPa @Treatment Temp. 100 °C, Time 3600 sec	36300 psi @Treatment Temp. 212 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	280 MPa @Treatment Temp. 50.0 °C, Time 3600 sec	40600 psi @Treatment Temp. 122 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
	300 MPa @Treatment Temp. 20.0 °C, Time 3600 sec	43500 psi @Treatment Temp. 68.0 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
Shear Strength	35.0 MPa @Thickness >=5.00 mm	5080 psi @Thickness >=0.197 in	24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO)	50.0 kJ/m² @Thickness >=5.00 mm	23.8 ft-lb/in² @Thickness >=0.197 in	24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	155 °C @Thickness 0.000 mm, Time 7.20e+7 sec	311 °F @Thickness 0.000 in, Time 20000 hour	IEC 60216; IEC/EN 60893-2 7.1
Flammability, UL94	V-0	V-0	IEC/EN 60893-2 7.2; IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Insulation Resistance	1.00e+9 ohm @Thickness >=3.00 mm	1.00e+9 ohm @Thickness >=0.118 in	24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3
Dielectric Constant	4.0 @Thickness <=3.00 mm, Frequency 50.0 Hz	4.0 @Thickness <=0.118 in, Frequency 50.0 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
	4.0 @Thickness <=3.00 mm, Frequency 1.00e+6 Hz	4.0 @Thickness <=0.118 in, Frequency 1.00e+6 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Dielectric Strength	2.40 kV/mm @Thickness >=3.00 mm	61.0 kV/in @Thickness >=0.118 in	24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2
	11.5 kV/mm @Thickness 3.00 mm	292 kV/in @Thickness 0.118 in	24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1
Dissipation Factor	0.040 @Frequency 50.0 Hz	0.040 @Frequency 50.0 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
	0.040 @Frequency 1.00e+6 Hz	0.040 @Frequency 1.00e+6 Hz	96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Comparative Tracking Index	600 V @Thickness 3.00 mm	600 V @Thickness 0.118 in	IEC 60112; IEC/EN 60893-2 6.4