LG Chemical LUPOL GP2200 PP+GF20%
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL GP2200 PP+GF20%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PP+GF20%, General PurposeApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 73.5 MPa @Thickness 3.20 mm |
10700 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 10 % @Thickness 3.20 mm |
>= 10 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 3.43 GPa @Thickness 6.40 mm |
498 ksi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.686 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
>= 1.29 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C @Thickness 3.20 mm |
302 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness >=1.50 mm |
149 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness >=1.50 mm |
149 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness >=1.50 mm |
149 °F @Thickness >=0.0591 in |
|
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Cellular E2000 Polyvinyl Chloride, Rigid (PVC, Rigid)
- SABIC Innovative Plastics Lexan® SLX1432D PC Copolymer
- Lehmann & Voss LUVOCOM® 1301-7508 PPS, linear, with glass spheres
- LG Chemical SEETEC H1500 Polypropylene Homopolymer
- Solvay Specialty Polymers Torlon® 4645 Polyamide-imide (PAI)
- Techmer ES HiFill® ABS HI 350 High Impact
- BASF Ultraform N 2640 Z6 UNC POM
- Braskem Green PE SLL118 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
- BASF Capron® 8332G Impact Modified, 25% Glass-Filled Nylon 6 (Dry) (discontinued **)
- DuPont Elvax® 760Q Ethylene Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved