Karina 802D35/1-E-AC-LF Ivory PVC Compound
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Wire and Cable Grade |
| Manufacturer | Karina Indústria e Comércio de Plásticos |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Karina 802D35/1-E-AC-LF Ivory PVC Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heavy metal free and flame retardant PVC compound, recommended for coaxial cables jackets.Information provided by Karina Indústria e Comércio de Plásticos Ltda.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 - 1.44 g/cc | 1.38 - 1.44 g/cc | NBR NM-IEC 60811-1-3 |
| ASTM Color | -1.96 - 1.04 | -1.96 - 1.04 | Color A, ME 12 |
| 0.89 - 3.89 | 0.89 - 3.89 | Color B, ME 12 | |
| 90.14 - 93.14 | 90.14 - 93.14 | Color L, ME 12 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 - 82 @Time 15.0 sec |
78 - 82 @Time 0.00417 hour |
NBR 7456 |
| Tensile Strength | >= 11.8 MPa | >= 1710 psi | After 168 H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
| >= 12.7 MPa | >= 1850 psi | NBR NM-IEC 60811-1-1 | |
| Elongation at Break | >= 200 % | >= 200 % | After 168H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
| >= 250 % | >= 250 % | NBR NM-IEC 60811-1-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Oxygen Index | >= 30 % | >= 30 % | NBR 6245 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D 257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Application | Coaxial |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 7518 C Natural Polypropylene
- Haynes 282® Nickel Alloy Sheet, Plate and Bar, Solution Annealed
- Techmer ES HiFill® PA6 GF/B20 A2 20% Glass Fiber/Glass Bead Filled
- A. Schulman POLYBATCH™ White LL8844 GP
- Arkema Group ORGASOL® 3501 EXD Nat 1 Copolyamide 6/12
- BASF Ultramid® B3WG7 BK 00564 35% Glass Filled PA6 (Conditioned)
- ArcelorMittal HSLA 260 High strength low alloy steel for cold forming, Cold Rolled
- Polyram RamOfin PPC350M6 Polypropylene, 30% Mineral Filled
- Chevron Phillips Marlex® M362 LLDPE Pipe and Corrugated Extrusion Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved