| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL ED1045D TPO, Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPO, Thermoplastic Elastomer, Soft TouchApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0, 1333-86-4, 25087-34-7 and 14807-96-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 12.7 MPa @Thickness 3.20 mm |
1850 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 200 % @Thickness 3.20 mm |
>= 200 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 5.88 MPa @Thickness 6.40 mm |
853 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| Flexural Modulus | 0.245 GPa @Thickness 6.40 mm |
35.6 ksi @Thickness 0.252 in |
30mm/min; ASTM D790 |
| Izod Impact, Notched | >= NB @Thickness 6.40 mm, Temperature 23.0 °C |
>= NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 210 - 230 °C | 410 - 446 °F | Injection Molding |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-60-30 Cellular Urethane Foam
- PolyOne Lubri-Tech™ PS-15GB/15T Polybutylene Terephthalate (PBT), Glass Bead Filled, PTFE Lubricated (discont
- ICE ZrO
- H.C. Starck Amperit® 827.054 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3)
- SABIC Innovative Plastics Valox® 325FC PBT (Europe-Africa-Middle East)
- Techmer ES Luriblend® PPA CF30 TL15 30% Carbon Filled
- EMS-Grivory Grivory® CF 7 PA*
- CMW® 100 Copper Alloy
- SABIC Innovative Plastics SABIC PPCOMPOUND 15T1040 PP
Copyright © lookpolymers.com All Rights Reserved