Samsung Cheil Industries Starex® VE-0812 ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® VE-0812 ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 37.3 MPa | 5400 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 6.35 mm |
2.76 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C @Thickness 6.40 mm |
178 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 91.0 °C | 196 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0 @Thickness 1.50 - 3.00 mm |
V-0 @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4807 TPE, Transparent
- SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer (Asia Pacific)
- SABIC Innovative Plastics Lexan® 925A PC (Asia Pacific)
- Samsung Cheil Industries Starex® BF-0677HF MABS, Unreinforced Scratch Resistant
- Voloknohim Filament Nylon Linear Density 117 tex
- A. Schulman POLYBATCH™ Green 3600 Concentrate Based In Polyethylene
- Eastman Embrace LV Copolyester for Extruded/Cast Film
- Aaron Industries AAROPRENE® CFIPP 2010 High Impact Calcium Carbonate Filled Polypropylene
- Beijing Chemical Industry KAIFA® MN201-G30 Nylon 66 Resin
Copyright © lookpolymers.com All Rights Reserved