LG Chemical LUMID LW4009A(W) PA6+GF/MF40%, Low Warpage
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID LW4009A(W) PA6+GF/MF40%, Low Warpage.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6+GF/MF40%, Low WarpageApplication: Automotive (Timing Belt Cover)CAS No. 25038-54-4, 13983-17-0 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Water Absorption | 0.90 % | 0.90 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.011 cm/cm @Thickness 3.20 mm |
0.0050 - 0.011 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 4.0 % @Thickness 3.20 mm |
4.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 196 MPa @Thickness 3.20 mm |
28400 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 7.35 GPa @Thickness 3.20 mm |
1070 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 1.00 mm |
533 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 245 - 265 °C | 473 - 509 °F | Injection Molding |
| Middle Barrel Temperature | 255 - 280 °C | 491 - 536 °F | Injection Molding |
| Front Barrel Temperature | 255 - 285 °C | 491 - 545 °F | Injection Molding |
| Nozzle Temperature | 255 - 285 °C | 491 - 545 °F | Injection Molding |
| Melt Temperature | 255 - 285 °C | 491 - 545 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® NX9240 PTFE Laminate, Woven-Glass Reinforced
- SABIC Innovative Plastics LNP STAT-KON DEL33EC PC (Asia Pacific)
- Silberline Aquavet® 205-136M
- Tra-Con Tra-Bond JL01 High Viscosity High Temperature Fiber Optic Adhesive
- DuPont Bynel® 30E670 Adhesive Resin
- ChevronTexaco NLGI 2 Ultra Duty Grease EP
- Akzo Nobel Trigonox® TAHP-W85 Polymerization Initiator
- 3M 410M Double Coated Paper Tapes
- Overview of materials for Nylon 6, Extruded
Copyright © lookpolymers.com All Rights Reserved