LATI Lastil G/25-V0 SAN, 25% Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | LATI |
| Trade Name | Lastil |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Lastil G/25-V0 SAN, 25% Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrene-Acrylonitrile copolymer (SAN) based compound. Glass fibers. UL94 V-0 classified, with brominated flame retardants. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0030 cm/cm | 0.0015 - 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0035 cm/cm | 0.0020 - 0.0035 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa @Temperature 90.0 °C |
8700 psi @Temperature 194 °F |
|
| 85.0 MPa @Temperature 60.0 °C |
12300 psi @Temperature 140 °F |
||
| 100 MPa @Temperature 23.0 °C |
14500 psi @Temperature 73.4 °F |
||
| Elongation at Break | 1.2 % @Temperature 23.0 °C |
1.2 % @Temperature 73.4 °F |
|
| 1.5 % @Temperature 60.0 °C |
1.5 % @Temperature 140 °F |
||
| 2.0 % @Temperature 90.0 °C |
2.0 % @Temperature 194 °F |
||
| Tensile Modulus | 6.80 GPa @Temperature 90.0 °C |
986 ksi @Temperature 194 °F |
|
| 8.50 GPa @Temperature 60.0 °C |
1230 ksi @Temperature 140 °F |
||
| 9.20 GPa @Temperature 23.0 °C |
1330 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Vicat Softening Point | 115 °C @Load 5.00 kg |
239 °F @Load 11.0 lb |
|
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| Oxygen Index | 28 % | 28 % | |
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
GWFI/GWT |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI/GWT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V | 250 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 220 °C | 374 - 428 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | |
| Drying Temperature | 70.0 - 80.0 °C @Time 10800 sec |
158 - 176 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1700-8019 PPO, with glass fiber and PTFE, low-warpage
- Mearthane Durethaneâ„¢ S DS-780DR Solid Polyurethane Elastomer
- Solvay Specialty Polymers Tecnoflon® FOR TF 636 Fluoroelastomer
- Solvay GEROPON® CYA/75 Surfactant
- ELASTO UK Dryflex® 602900S SEBS Based Material, Filled Qualities, 90A Hardness, Black
- Eurotec® Tecomid® NA40 NL XA70 PA6.6, unfilled, flame retardant - halogen free (RoHS compliant), heat stabilized, natural
- Chi Mei Wonderlite® PC-110N Polycarbonate - Flame Retardant
- Clariant Renol 6608G43 Nylon 66, 43% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated
- China-Yixing Longly Refractories Alumina Grinding Balls and Lining Bricks Microcrystal Wear-Resistant Alumina Grinding Media (Balls) and Lining Bricks
Copyright © lookpolymers.com All Rights Reserved