LG Chemical LUMID GP3200B(W) PA66+MF20%, General Purpose
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID GP3200B(W) PA66+MF20%, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6+MF20%, General PurposeApplication: E&E (Rice Cooker Housing)Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | ASTM D570 |
| Maximum Moisture Content | 0.090 | 0.090 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.010 - 0.012 cm/cm @Thickness 3.20 mm |
0.010 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 79.4 MPa @Thickness 3.20 mm |
11500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 8.0 % @Thickness 3.20 mm |
8.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 3.92 GPa @Thickness 3.20 mm |
569 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C @Thickness 6.40 mm |
446 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm @Thickness 1.00 mm |
508 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 265 - 275 °C | 509 - 527 °F | Injection Molding |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Front Barrel Temperature | 270 - 285 °C | 518 - 545 °F | Injection Molding |
| Nozzle Temperature | 270 - 295 °C | 518 - 563 °F | Injection Molding |
| Melt Temperature | 270 - 275 °C | 518 - 527 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer (Europe-Africa-Middle East)
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 10% Plasticizer (discontinued **)
- Mateck Fused Silica IR Grade (SiO2)
- Techmer ES HiFill® PA6 HS L Colors Heat Stabilized
- Teknor Apex Monprene® MP-1846-L3 Thermoplastic Elastomer
- Saint-Gobain Chemfab® 10 Premium PTFE-Coated Glass
- SABIC Innovative Plastics NORYL 844 PPE+PS (Asia Pacific)
- Teknor Apex Telcar® TL-1524F Thermoplastic Elastomer
- Ametek P316L P/M Stainless Steel, Sintered from 6.25 g/cc Green Density
- AIM SAC305 Lead-Free Solder for Photonic Packaging
Copyright © lookpolymers.com All Rights Reserved