Polyram PlusTek PA340S4 Nylon 66 for Injection Molding, 20% Glass-Beads Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA340S4 Nylon 66 for Injection Molding, 20% Glass-Beads Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass-beads reinforced Nylon 66 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 4.14 GPa | 600 ksi | ISO 527 |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| Flexural Modulus | 4.135 GPa | 599.7 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.70 kJ/m² | 1.76 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Glow Wire Test | 650 °C | 1200 °F | GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- MV Labs TM100 Tm(C2H3O2)3·xH2O Thulium acetate hydrate
- 3M Dyneon™ TF 5041 PTFE Dispersion (discontinued **)
- Lehmann & Voss LUVOCOM® 1-7791 Polyamide 66, with carbon fiber, PTFE, lubricant modified, heat stabilized
- Williams Advanced Alloys Wambraze™ WB1030 Solder
- DuPont Teijin Films Mylar® MO Polyester Film, 500 Gauge
- Abatron AboSeal 8104-17 Acrylic-Latex Based Sealant and Caulk; High-Density
- 3M Scotchkote™ UV 840 Urethane Coating
- Beijing Evergrow Resources ACFCC-1100 Activated Carbon Fiber Composite Cloth
Copyright © lookpolymers.com All Rights Reserved