LG Chemical LUCEL N109LD POM, Chemical Resistance

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer LG Chemical
Trade Name LUCEL
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUCEL N109LD POM, Chemical Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Feature: Injection Molding, POM, Chemical ResistanceApplication: Copier, Watch, Clock, VCR, Printer Parts, etc.CAS No. 66455-31-0Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ASTM D792
Maximum Moisture Content 0.10
0.10
Injection Molding
Linear Mold Shrinkage, Flow 0.018 - 0.021 cm/cm
<br>@Thickness 3.20 mm
 0.018 - 0.021 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 9.0 g/10 min
<br>@Load 2.16 kg,<br> Temperature 190 °C
 9.0 g/10 min
<br>@Load 4.76 lb,<br> Temperature 374 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 82
82
ASTM D785
Tensile Strength, Yield 60.8 MPa
<br>@Thickness 3.20 mm
 8820 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D638
Elongation at Break 65 %
<br>@Thickness 3.20 mm
 65 %
<br>@Thickness 0.126 in
 10mm/min; ASTM D638
Flexural Yield Strength 89.2 MPa
<br>@Thickness 6.40 mm
 12900 psi
<br>@Thickness 0.252 in
 2.8mm/min; ASTM D790
Flexural Modulus 2.55 GPa
<br>@Thickness 6.40 mm
 370 ksi
<br>@Thickness 0.252 in
 2.8mm/min; ASTM D790
Izod Impact, Notched 0.686 J/cm
<br>@Thickness 6.40 mm,<br> Temperature 23.0 °C
 1.29 ft-lb/in
<br>@Thickness 0.252 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
<br>@Thickness 6.40 mm
 320 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
<br>@Thickness 6.40 mm
 230 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 110 °C
<br>@Thickness >=0.710 mm
 230 °F
<br>@Thickness >=0.0280 in
110 °C
<br>@Thickness >=1.50 mm
 230 °F
<br>@Thickness >=0.0591 in
110 °C
<br>@Thickness >=3.00 mm
 230 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical with Impact 95.0 °C
<br>@Thickness >=0.710 mm
 203 °F
<br>@Thickness >=0.0280 in
95.0 °C
<br>@Thickness >=1.50 mm
 203 °F
<br>@Thickness >=0.0591 in
95.0 °C
<br>@Thickness >=3.00 mm
 203 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact 100 °C
<br>@Thickness >=0.710 mm
 212 °F
<br>@Thickness >=0.0280 in
100 °C
<br>@Thickness >=1.50 mm
 212 °F
<br>@Thickness >=0.0591 in
100 °C
<br>@Thickness >=3.00 mm
 212 °F
<br>@Thickness >=0.118 in
Flammability, UL94 HB
<br>@Thickness >=0.710 mm
 HB
<br>@Thickness >=0.0280 in
HB
<br>@Thickness >=1.50 mm
 HB
<br>@Thickness >=0.0591 in
HB
<br>@Thickness >=3.00 mm
 HB
<br>@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Constant 3.8
<br>@Frequency 1.00e+6 Hz
 3.8
<br>@Frequency 1.00e+6 Hz
 ASTM D150
Dielectric Strength 24.0 kV/mm
<br>@Thickness 1.00 mm
 610 kV/in
<br>@Thickness 0.0394 in
 ASTM D149
Hot Wire Ignition, HWI 0.00 - 7.0 sec
<br>@Thickness >=0.710 mm
 0.00 - 7.0 sec
<br>@Thickness >=0.0280 in
7.0 - 15 sec
<br>@Thickness >=3.00 mm
 7.0 - 15 sec
<br>@Thickness >=0.118 in
7.0 - 15 sec
<br>@Thickness >=1.50 mm
 7.0 - 15 sec
<br>@Thickness >=0.0591 in
High Amp Arc Ignition, HAI >= 120 arcs
<br>@Thickness 3.00 mm
 >= 120 arcs
<br>@Thickness 0.118 in
>= 120 arcs
<br>@Thickness 1.50 mm
 >= 120 arcs
<br>@Thickness 0.0591 in
>= 120 arcs
<br>@Thickness 0.710 mm
 >= 120 arcs
<br>@Thickness 0.0280 in
Processing Properties Metric English Comments
Rear Barrel Temperature 160 - 180 °C
320 - 356 °F
Injection Molding
Middle Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Front Barrel Temperature 190 - 200 °C
374 - 392 °F
Injection Molding
Nozzle Temperature 190 - 200 °C
374 - 392 °F
Injection Molding
Melt Temperature 190 - 200 °C
374 - 392 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 90.0 - 110 °C
194 - 230 °F
Injection Molding
Dry Time 3.00 - 6.00 hour
3.00 - 6.00 hour
Injection Molding
Back Pressure 4.02 - 8.04 MPa
583 - 1170 psi
Injection Molding
Screw Speed 50 - 100 rpm
50 - 100 rpm
Injection Molding