LG Chemical LUCEL HI525L POM+Rubber, High Impact
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | LG Chemical |
| Trade Name | LUCEL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCEL HI525L POM+Rubber, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, POM+Rubber, High ImpactApplication: GearsCAS No. 66455-31-0 and 155123-66-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.10 | 0.10 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.017 - 0.020 cm/cm @Thickness 3.20 mm |
0.017 - 0.020 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 64 | 64 | ASTM D785 |
| Tensile Strength, Yield | 36.2 MPa @Thickness 3.20 mm |
5250 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 85 % @Thickness 3.20 mm |
85 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 40.4 MPa @Thickness 3.20 mm |
5860 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 1.1946 GPa @Thickness 3.20 mm |
173.27 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.794 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
1.49 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C @Thickness 6.40 mm |
165 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| Front Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Nozzle Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Dry Time | 2.00 - 3.00 hour | 2.00 - 3.00 hour | Injection Molding |
| Back Pressure | 0.490 - 3.04 MPa | 71.1 - 441 psi | Injection Molding |
| Screw Speed | 80 - 110 rpm | 80 - 110 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IE6010 Unitape Unidirectional Polypropylene-Glass Composite
- Premix Thermoplastics PRE-ELEC® ESD 7120
- Iran Petrochemical (PCC) Tabriz 4240/1 High Impact Polystyrene (discontinued **)
- Sylvin Technologies 8960-80 Natural PVC Extrusion Compound
- Solvay TECHNYL® A 218 V35 Black 21NHFE PA66, 35% glass fiber, Conditioned
- SABIC Innovative Plastics NORYL WCD933 PPE-TPE
- SABIC Innovative Plastics Valox® DR48M PBT (Asia Pacific)
- Unipetrol A+ High-Conductive Carbon Black Chezacarb
- Colorite Polymers Flexchem 6051-02 Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved