Chosun Refractories PT-165 Plastic Refractory
| Category | Ceramic , Oxide , Silicon Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories PT-165 Plastic Refractory.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 3.85e-7 - 0.000981 GPa @Temperature 110 °C, Time 86400 sec |
0.0000558 - 0.142 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.002943 - 0.005886 GPa @Temperature 1350 °C, Time 10800 sec |
0.4269 - 0.8537 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.004905 - 0.007848 GPa @Temperature 1500 °C, Time 10800 sec |
0.7114 - 1.138 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 4.90 - 9.81 MPa @Temperature 110 °C, Time 86400 sec |
711 - 1420 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 19.6 - 29.4 MPa @Temperature 1350 °C, Time 10800 sec |
2840 - 4270 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 24.5 - 34.3 MPa @Temperature 1500 °C, Time 10800 sec |
3560 - 4980 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.97705 W/m-K @Temperature 500 °C |
6.7697 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| 1.0585 W/m-K @Temperature 1000 °C |
7.3339 BTU-in/hr-ft²-°F @Temperature 1830 °F |
||
| Maximum Service Temperature, Air | 1650 °C | 3000 °F | limited |
| Shrinkage | -0.700 % @Temperature 110 °C, Time 86400 sec |
-0.700 % @Temperature 230 °F, Time 24.0 hour |
|
| 0.20 % @Temperature 1500 °C, Time 10800 sec |
0.20 % @Temperature 2730 °F, Time 3.00 hour |
||
| 0.30 % @Temperature 1350 °C, Time 10800 sec |
0.30 % @Temperature 2460 °F, Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 43 % | 43 % | |
| SiO2 | 50 % | 50 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Main Applications | Heat set Air Set Spalling resistance Volume stability Various furnace | |
| Material Required for Estimating (kg/?) | 2,400 |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ NN-20SS/000 Black Polyamide 66 (Nylon 66)
- PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced (discontinued **)
- Kotec Carbotex KGN-10MRA Polycarbonate, Flame Retardant, 10% Glass Fiber Reinforced
- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
- Unifrax Fiberfrax® Bulk 7000 High Purity Bulk Fiber
- American Computer Optics Water White Filter 3 mm
- A. Schulman ComAlloy Hiloy® 638 Nylon 6/6, Mineral Reinforced, Flow Enhanced
- Isoflon ETFE
- Materion Beryllium Copper Alloy 3 Wire; HT (TH04) Temper; 1.3-12.7 mm Diameter (UNS C17510)
Copyright © lookpolymers.com All Rights Reserved