LG Chemical KEYFLEX TO1088AV Olefin Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Olefinic TPE , Thermoplastic Vulcanizate Elastomer (TPV) |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX TO1088AV Olefin Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPV, General Purpose, Soft TouchApplication: Automotive InteriorCAS: 9003-07-0Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 100 g/10 min @Load 10.0 kg, Temperature 230 °C |
100 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 - 91 | 85 - 91 | ASTM D2240 |
| Tensile Strength at Break | 8.34 MPa @Thickness 2.00 mm |
1210 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 300 % @Thickness 2.00 mm |
300 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Izod Impact, Notched | NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature -40.0 °C |
NB @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Injection Molding |
| Front Barrel Temperature | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| Nozzle Temperature | 200 - 240 °C | 392 - 464 °F | Injection Molding |
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Heatbath/Park Partherm 350 Heat Transfer Salt
- SABIC Innovative Plastics Xylex X7509UV PC+POLYESTER (Asia Pacific)
- Samsung Cheil Industries Starex® GA-4025 ABS, 25% Glass Filled
- Williams Advanced Alloys WS280B Solder (Au80/Sn20)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 3.0 PHR MBT
- ChevronTexaco 150 PMO Premium
- Arlon 51393R031 0.031 (0.635 mm) Cured Silicone Rubber with Fiberglass Substrate
- Bayshore Vinyl Compounds BVC 6200-65 Vinyl Compound
- BCC Products BC 8400 Urethane Casting
- Huntsman Rexell® V3401 Blown Film Extrusion LLDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved