LyondellBasell Hostacomâ„¢ TKS708D Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hostacom™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hostacomâ„¢ TKS708D Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hostacomâ„¢ TKS708D medium high melt flow, 1,300 MPa flexural modulus, UV-stabilized, high impact thermoplastic elastomeric olefin (TEO) resin has an excellent combination of properties and processability. It was designed for applications that require good low temperature impact resistance, moderate rigidity, and excellent aesthetics.Information provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ISO 1183 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ISO 527-1, -2 |
| Elongation at Break | 400 % | 400 % | ISO 527-1, -2 |
| Elongation at Yield | 10 % | 10 % | ISO 527-1, -2 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 0.000 °C |
1.43 ft-lb/in² @Temperature 32.0 °F |
ISO 180 |
| 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 25.0 J @Temperature 0.000 °C |
18.4 ft-lb @Temperature 32.0 °F |
Instrumented Energy at Maximum Load; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.8 °C | 199 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 1.1 % | 1.1 % | Tool; Basell Test Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | >= 85 % | >= 85 % | 60°, Gardner gloss; ASTM D523 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-50-30 Cellular Urethane Foam
- Precision Polymer Engineering S65Z Silicone Rubber
- Polymer Resources PC/ABS-G10 General Purpose PC/ABS Alloy, 10% Glass Filled
- Solvay Specialty Polymers Polidan® EC/51 Polyethylene, Crosslinked (XLPE)
- Shakespeare Resistat® F9222 B040 Nylon 6 Monofilament
- A. Schulman LP479-01 High-Density Polyethylene Homopolymer
- Eastman Tenite 360E2R30016 Cellulose Acetate Propionate, Natural, Trsp
- Addiplast Addilene PMD 50258 Polypropylene Copolymer
- A. Schulman ComAlloy Hiloy® 617 Nylon 6, Glass/Mineral Reinforced, UL
- SABIC Innovative Plastics LNP Verton PV00A PA 6 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved