LG Chemical ALPHALAC SF510 HIPS

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Grade, Glass Filled
Manufacturer LG Chemical
Trade Name ALPHALAC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical ALPHALAC SF510 HIPS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Super flow, High gloss and high impact equivalent to ABS, Excellent mechanical properties compare with general HIPS, Meet requirements for cost and quality, Applications include TV cabinets, thin part, and high speed injection moldingCAS No. 9003-55-8Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Melt Flow 12 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238(G)
34 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 34 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238(I)
137 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 137 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238(G)
Mechanical Properties Metric English Comments
Hardness, Rockwell R 101
101
ASTM D785
Tensile Strength, Yield 26.5 MPa

@Thickness 3.20 mm
 3840 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 51 %

@Thickness 3.20 mm
 51 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Yield 5.0 %

@Thickness 3.20 mm
 5.0 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Tensile Modulus 2.11 GPa

@Thickness 3.20 mm
 306 ksi

@Thickness 0.126 in
 1mm/min; ASTM D638
Flexural Yield Strength 42.2 MPa

@Thickness 3.20 mm
 6120 psi

@Thickness 0.126 in
 15mm/min; ASTM D790
Flexural Modulus 2.30 GPa

@Thickness 3.20 mm
 334 ksi

@Thickness 0.126 in
 15mm/min; ASTM D790
Izod Impact, Notched 0.490 J/cm

@Thickness 6.50 mm,
Temperature -30.0 °C
 0.918 ft-lb/in

@Thickness 0.256 in,
Temperature -22.0 °F
 ASTM D256
0.686 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 1.29 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
0.981 J/cm

@Thickness 6.50 mm,
Temperature 23.0 °C
 1.84 ft-lb/in

@Thickness 0.256 in,
Temperature 73.4 °F
 ASTM D256
1.37 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 2.57 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 89.0 °C

@Thickness 6.40 mm
 192 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C

@Thickness 6.40 mm
 176 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 88.0 °C

@Load 5.00 kg
 190 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=1.50 mm
 7.0 - 15 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
 15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 1.50 mm
 60 - 120 arcs

@Thickness 0.0591 in
60 - 120 arcs

@Thickness 3.00 mm
 60 - 120 arcs

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 170 - 190 °C
338 - 374 °F
Injection Molding
Middle Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Nozzle Temperature 190 - 220 °C
374 - 428 °F
Injection Molding
Melt Temperature 190 - 220 °C
374 - 428 °F
Injection Molding
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding