Solvay Specialty Polymers Amodel® ET-1001 HS Polyphthalamide (PPA) Resin, Dry As Molded  (discontinued **)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), High Impact
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® ET-1001 HS Polyphthalamide (PPA) Resin, Dry As Molded  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL ET-1001 HS resin is an impact modified polyphthalamide (PPA) with exceptional impact strength and practical toughness. AMODEL PPA resins offer high fatigue strength, and good chemical resistance combined with good mechanical property retention over a broad temperature/humidity range. Possible applications for AMODEL ET-1001 HS resin include: anti-friction and wear resistant components, and components of chemical and oil processing equipment, sporting goods, automobiles, household appliances, power tools, and safety equipment, where exceptional impact strength and high modulus are required. AMODEL ET-1001 HS resin contains a lubricant for easier processing with conventional equipment and methods. This grade is also heat stabilized for better performance at high temperatures.This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.MatWeb has an entry for this material conditioned at 50% RH.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ASTM D792
Water Absorption 0.65 %
0.65 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.020 cm/cm
0.020 in/in
ASTM E831
Linear Mold Shrinkage, Transverse 0.020 cm/cm
0.020 in/in
ASTM E831
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 76.0 MPa
11000 psi
ASTM D638
Elongation at Break 30 %
30 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
ASTM D638
Flexural Yield Strength 128 MPa
18600 psi
ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
ASTM D790
Poissons Ratio 0.35
0.35
Shear Modulus 0.889 GPa
129 ksi
Calculated
Izod Impact, Notched 9.60 J/cm
18.0 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 321 - 343 °C
610 - 649 °F
Injection