POLYMER SEARCH

LATI Latistat 52/7-02 PP Homopolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer	LATI
Trade Name	Latistat
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latistat 52/7-02 PP Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Dissipative product based on Polypropylene homopolymer (PPh). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	0.950 g/cc	0.0343 lb/inÂ³
Linear Mold Shrinkage, Flow	0.015 - 0.018 cm/cm	0.015 - 0.018 in/in
Linear Mold Shrinkage, Transverse	0.0155 - 0.0185 cm/cm	0.0155 - 0.0185 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	35.0 MPa	5080 psi
Elongation at Break	3.5 %	3.5 %
Elongation at Yield	2.0 %	2.0 %
Tensile Modulus	2.70 GPa	392 ksi
Charpy Impact Unnotched	2.50 J/cmÂ²	11.9 ft-lb/inÂ²
Charpy Impact, Notched	0.200 J/cmÂ²	0.952 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	115 Â°C	239 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	75.0 Â°C	167 Â°F
Vicat Softening Point	115 Â°C @Load 5.00 kg	239 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	50 ohm	50 ohm

Processing Properties	Metric	English
Melt Temperature	180 - 220 Â°C	356 - 428 Â°F
Mold Temperature	20.0 - 40.0 Â°C	68.0 - 104 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa