- PolyOne Edgetek® NJ-000/000 Nylon 12 (discontinued **)
PolyOne Edgetek® NJ-000/000 Nylon 12 (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® NJ-000/000 Nylon 12
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:General Purpose GradeHeat StabilizedHigh FlowUL 94 HBProcessing Method:Injection MoldingPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Water Absorption | 0.80 % | 0.80 % | 24 hr. Immersion; ASTM D570 |
| Water Absorption at Saturation | 1.5 % | 1.5 % | Long-Term Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 53.8 MPa | 7800 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 250 % | 250 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 5.45 MPa | 790 psi | ASTM D790 |
| Flexural Modulus | 1.42 GPa | 206 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.900 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 °C | 450 °F | Molding |
| Drying Temperature | 54.4 °C | 130 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Petromont 1002 High Density Polyethylene Resin
- Polymer Resources NY6-M25G15 Nylon 6, 25% Mineral, 15% Glass Reinforced
- Solvay ALKAMULS® EL 620 Surfactant
- A. Schulman POLYBATCH™ Light Blue 40442 Concentrate Based In LLDPE
- Zoltek Panex 35® Type 85 Chopped Carbon Fiber for High-Temperature Thermoplastics
- Ensinger HYDLAR® Z Nylon, Pultruded Aramid Fiber Reinforced (PA)
- Devcon Brushable Ceramic - White Epoxy
- Dow DOWLEX™ NG 3347A Linear Low Density Polyethylene, Ethylene-Octene Copolymer
- Dow Corning 3715 TOPCOAT
- 3M FM069 Indoor UL Recognized Brite Silver Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved