SABIC Innovative Plastics Ultem JD7902 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem JD7902 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D 792 |
| Water Absorption | 0.26 % @Time 86400 sec |
0.26 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 127 MPa | 18400 psi | SABIC - Japan Method |
| Elongation at Break | 5.0 % | 5.0 % | SABIC - Japan Method |
| Flexural Strength | 186 MPa | 27000 psi | ASTM D 790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.490 J/cm @Temperature 23.0 °C |
0.918 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+6 - 1.00e+8 ohm | 1.00e+6 - 1.00e+8 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 85FS GF10 PC/ABS-Blend, Glass Fiber reinforced
- SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66
- Samsung Cheil Industries Infino® UF-1017 PC, Unreinforced FR
- Supreme Petrochem SH 2114 High Impact Polystyrene
- Zhejiang Juner PC Alloy
- A. Schulman POLYFORT™ FPP 1609 Mica Fortified Copolymer Polypropylene
- Covestro Apec® 1895 Polycarbonate
- Fainplast Compounds GS 7503 Flexible PVC, Injection Molding for Footwear
- Bapolene® 4052F Polypropylene, Blown Film Grade
- Ashley Polymers Ashlene® D925 Nylon 12
Copyright © lookpolymers.com All Rights Reserved