Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | ULTEM |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics ULTEM 1000EF PEI (Europe-Africa-Middle East).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
Water Absorption | 0.25 % @Time 86400 sec |
0.25 % @Time 24.0 hour |
ASTM D570 |
Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
Moisture Absorption at Equilibrium | 1.25 % | 1.25 % | ASTM D570 |
Water Absorption at Saturation | 1.25 % | 1.25 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
Melt Flow | 12 g/10 min @Load 6.60 kg, Temperature 337 °C |
12 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 360 °C |
17 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D638 |
85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | |
Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | |
Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D638 |
60 % | 60 % | 5 mm/min; ISO 527 | |
Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |
Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
3.59 GPa | 521 ksi | 5 mm/min; ASTM D638 | |
Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
3.52 GPa | 511 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
13.35 J/cm @Thickness 3.20 mm |
25.01 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
Izod Impact, Unnotched | 13.35 J/cm | 25.01 ft-lb/in | ASTM D4812 |
Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
Dart Drop, Total Energy | 38.0 J @Temperature 23.0 °C |
28.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
55.0 µm/m-°C @Temperature 23.0 - 150 °C |
30.6 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
55.0 µm/m-°C @Temperature 23.0 - 150 °C |
30.6 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C177 |
0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ISO 8302 | |
Deflection Temperature at 0.46 MPa (66 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
200 °C | 392 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | |
207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
201 °C @Thickness 6.40 mm |
394 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
Vicat Softening Point | 211 °C | 412 °F | Rate B/50; ISO 306 |
212 °C | 414 °F | Rate B/120; ISO 306 | |
215 °C | 419 °F | Rate A/50; ISO 306 | |
219 °C | 426 °F | Rate B/50; ASTM D1525 | |
Glass Transition Temp, Tg | 217 °C | 423 °F |
Optical Properties | Metric | English | Comments |
---|---|---|---|
Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Descriptive Properties | Value | Comments |
---|---|---|
Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |