LATI Latilub 73/13-01M POM, Molybdenum disulphide Filled

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 73/13-01M POM, Molybdenum disulphide Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyoxymethylene (POM). Molybdenum disulphide. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.44 g/cc	0.0520 lb/inÂ³
Linear Mold Shrinkage, Flow	0.020 - 0.023 cm/cm	0.020 - 0.023 in/in
Linear Mold Shrinkage, Transverse	0.0205 - 0.0225 cm/cm	0.0205 - 0.0225 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	65.0 MPa	9430 psi
Elongation at Break	20 %	20 %
Elongation at Yield	5.0 %	5.0 %
Tensile Modulus	2.60 GPa	377 ksi
Charpy Impact Unnotched	5.00 J/cmÂ²	23.8 ft-lb/inÂ²
Charpy Impact, Notched	0.580 J/cmÂ²	2.76 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.16	0.16
Coefficient of Friction, Static	0.18	0.18
K (wear) Factor	11.0 x 10^-8 mmÂ³/N-M	5.46 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	110 Â°C	230 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	85.0 Â°C	185 Â°F
Vicat Softening Point	130 Â°C @Load 5.00 kg	266 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	175 - 200 Â°C	347 - 392 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa