LG Chemical PI641 ABS, High Impact
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical PI641 ABS, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Extrusion Molding, General Purpose, High ImpactApplication: Pipe FittingCAS No. 9003-56-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Extrusion Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 45.1 MPa @Thickness 3.20 mm |
6540 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 20 % @Thickness 3.20 mm |
20 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Elongation at Yield | >= 5.0 % @Thickness 3.20 mm |
>= 5.0 % @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| Flexural Yield Strength | 68.6 MPa @Thickness 3.20 mm |
9960 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Flexural Modulus | 2.30 GPa @Thickness 3.20 mm |
334 ksi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
| Izod Impact, Notched | 4.12 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
7.71 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 4.41 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
8.27 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 94.0 °C @Load 5.00 kg |
201 °F @Load 11.0 lb |
50°C/h; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 210 °C | 356 - 410 °F | Extrusion Molding |
| Zone 2 | 190 - 230 °C | 374 - 446 °F | Extrusion Molding |
| Zone 3 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Zone 4 | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Adapter Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Die Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | Extrusion Molding |
| Roll Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Bottom, Extrusion |
| 70.0 - 90.0 °C | 158 - 194 °F | Middle, Extrusion | |
| 70.0 - 100 °C | 158 - 212 °F | Top, Extrusion | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Extrusion Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- NextGen Adhesives G907-27 Structural Adhesive
- Polymer Industries Densetec HDPE Playground Board
- Huntsman HY 2963 Cycloaliphatic Amine
- SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS
- Techmer ES Electrablend® PPS 06001
- UBE UBESTA® 3030U Nylon 12 (After Hydrochloric Acid (10%) for 500 hours)
- Entec Hypro™ PP-CP10/10 Impact Copolymer, 10 Melt Flow
- Adell BR-34 Nylon 6, 20% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved