POLYMER SEARCH

LATI Latilub 66-20ST PA66, Silicone/PTFE Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 66-20ST PA66, Silicone/PTFE Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyamide 66 (PA66). Silicone / PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.26 g/cc	0.0455 lb/inÂ³
Linear Mold Shrinkage, Flow	0.013 - 0.016 cm/cm	0.013 - 0.016 in/in
Linear Mold Shrinkage, Transverse	0.014 - 0.017 cm/cm	0.014 - 0.017 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	75.0 MPa	10900 psi
Elongation at Break	5.0 %	5.0 %
Elongation at Yield	2.0 %	2.0 %
Tensile Modulus	2.80 GPa	406 ksi
Charpy Impact Unnotched	4.50 J/cmÂ²	21.4 ft-lb/inÂ²
Charpy Impact, Notched	0.500 J/cmÂ²	2.38 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.16	0.16
Coefficient of Friction, Static	0.20	0.20
K (wear) Factor	7.20 x 10^-8 mmÂ³/N-M	3.57 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	250 Â°C	482 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	100 Â°C	212 Â°F
Vicat Softening Point	245 Â°C @Load 5.00 kg	473 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	270 - 300 Â°C	518 - 572 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa