LATI Laticonther 62 CEG/500-V0HF1 PA 6, Glass/Mineral Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer LATI
Trade Name Laticonther
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Laticonther 62 CEG/500-V0HF1 PA 6, Glass/Mineral Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
High thermal conductivity product based on Polyamide 6 (PA6). Glass fibers / Mineral filler. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0045 cm/cm
0.0030 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0065 cm/cm
0.0050 - 0.0065 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa
<br>@Temperature 150 °C
 5080 psi
<br>@Temperature 302 °F
45.0 MPa
<br>@Temperature 120 °C
 6530 psi
<br>@Temperature 248 °F
55.0 MPa
<br>@Temperature 90.0 °C
 7980 psi
<br>@Temperature 194 °F
65.0 MPa
<br>@Temperature 60.0 °C
 9430 psi
<br>@Temperature 140 °F
85.0 MPa
<br>@Temperature 23.0 °C
 12300 psi
<br>@Temperature 73.4 °F
Elongation at Break 1.5 %
<br>@Temperature 23.0 °C
 1.5 %
<br>@Temperature 73.4 °F
1.8 %
<br>@Temperature 60.0 °C
 1.8 %
<br>@Temperature 140 °F
2.0 %
<br>@Temperature 90.0 °C
 2.0 %
<br>@Temperature 194 °F
2.5 %
<br>@Temperature 120 °C
 2.5 %
<br>@Temperature 248 °F
2.5 %
<br>@Temperature 150 °C
 2.5 %
<br>@Temperature 302 °F
Tensile Modulus 2.80 GPa
<br>@Temperature 150 °C
 406 ksi
<br>@Temperature 302 °F
3.50 GPa
<br>@Temperature 120 °C
 508 ksi
<br>@Temperature 248 °F
4.70 GPa
<br>@Temperature 90.0 °C
 682 ksi
<br>@Temperature 194 °F
6.50 GPa
<br>@Temperature 60.0 °C
 943 ksi
<br>@Temperature 140 °F
10.5 GPa
<br>@Temperature 23.0 °C
 1520 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²
<br>@Temperature 23.0 °C
 7.14 ft-lb/in²
<br>@Temperature 73.4 °F
1.50 J/cm²
<br>@Temperature -20.0 °C
 7.14 ft-lb/in²
<br>@Temperature -4.00 °F
Charpy Impact, Notched 0.350 J/cm²
<br>@Temperature 23.0 °C
 1.67 ft-lb/in²
<br>@Temperature 73.4 °F
0.350 J/cm²
<br>@Temperature -20.0 °C
 1.67 ft-lb/in²
<br>@Temperature -4.00 °F
Thermal Properties Metric English Comments
Thermal Conductivity 1.10 W/m-K
7.63 BTU-in/hr-ft²-°F
Longitudinal
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Vicat Softening Point 210 °C
<br>@Load 5.00 kg
 410 °F
<br>@Load 11.0 lb
Flammability, UL94 V-1
<br>@Thickness 0.750 mm
 V-1
<br>@Thickness 0.0295 in
V-0
<br>@Thickness 3.00 mm
 V-0
<br>@Thickness 0.118 in
V-0
<br>@Thickness 1.50 mm
 V-0
<br>@Thickness 0.0591 in
Oxygen Index 42 %
42 %
Glow Wire Test 775 °C
<br>@Thickness 1.00 mm
 1430 °F
<br>@Thickness 0.0394 in
 GWIT
960 °C
<br>@Thickness 1.00 mm
 1760 °F
<br>@Thickness 0.0394 in
 GWFI/GWT
960 °C
<br>@Thickness 2.00 mm
 1760 °F
<br>@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C
<br>@Time 10800 sec
 194 - 212 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa