Samyang Triel® 5500 Thermoplastics Polyetherester Elastomer, General Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5500 Thermoplastics Polyetherester Elastomer, General Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5500 is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 - 0.017 cm/cm | 0.015 - 0.017 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 15 g/10 min @Load 2.16 kg, Temperature 240 °C |
15 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength, Ultimate | 24.5 MPa | 3560 psi | ASTM D638 |
| Tensile Strength, Yield | 9.81 MPa @Strain 5.00 % |
1420 psi @Strain 5.00 % |
ASTM D638 |
| 12.7 MPa @Strain 10.0 % |
1850 psi @Strain 10.0 % |
ASTM D638 | |
| 15.7 MPa @Strain 50.0 % |
2280 psi @Strain 50.0 % |
ASTM D638 | |
| Flexural Yield Strength | 7.85 MPa | 1140 psi | ASTM D790 |
| Flexural Modulus | 0.145 GPa | 21.1 ksi | ASTM D790 |
| Izod Impact, Notched | NB @Thickness 3.17 mm, Temperature -40.0 °C |
NB @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 3.17 mm, Temperature 23.0 °C |
NB @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 °C | 410 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Vicat Softening Point | 174 °C | 345 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- Polykemi AB SCANBLEND FS8 FR UV PC/ASA, Flame Retardant, UV-Stabilized
- Petroquimica Triunfo Trithene® TU 3001 LDPE - Agricultural Film
- PolyOne Therma-Tech™ SF-6000 TC Polyphenylene Sulfide (PPS) (discontinued **)
- Kennametal Stellite Delcrome® 93
- Industrial Laminates/Norplex NP510A Glass Fabric
- LATI Latistat 62-06 K/10 PA6, 10% Carbon Fiber Reinforced
- Teknor Apex APEX® RE 9016A Polyvinyl Chloride, Rigid
- Skamol Group Moler BB-BLOCK Insulating Block
- Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Sheets
- RheTech Products G20P252-00 20% Glass Fiber Reinforced Polypropylene Copolymer, Natural
Copyright © lookpolymers.com All Rights Reserved